Séminaire Prof. Yong ZHANG - Mercredi 28 Novembre 2018

par Christelle FLOUTIER -

Mercredi 28 Novembre 2018 à 14h
Séminaire Professeur Yong ZHANG
School of Chemistry and Chemical Engineering
Shanghai Jiao Tong University, Shanghai - China.


Plasticization and Toughening Modification of Poly(lactic acid) as Biodegradable Plastics


Poly(lactic acid) is a biodegradable polyester from renewable resources with a glass transition temperature at about 60°C and becomes a promising material for its high strength, modulus, and excellent transparency. Except for its well-known medical applications, its usage as a commodity plastic with high productivity is approaching. The plasticization and toughening modification of poly(lactic acid) is carried out to meet the need of its usage in plastics with varied hardness and impact strength. Poly(butylene succinate)-grafted cellulose nanocrystal and dicumyl peroxide exhibit great effects on the mechanical properties of poly(lactic acid).

References :

1) 1) Zhang, Xuzhen ; Zhang, Yong*. Reinforcement effect of poly(butylene succinate) (PBS)-grafted cellulose nanocrystal on toughened PBS/poly(lactic acid) blends. Carbohydrate Polymers. 140, 374–382, 2016.
2) Wang, RY ; Wan, CY ; Wang, SF, Zhang, Y*. Morphology, Mechanical Properties, and Durability of Poly(Lactic Acid) Plasticized With Di(Isononyl) Cyclohexane-1,2-Dicarboxylate. Polymer Engineering and Science. 49, 2414-2420, 2009
3) Wang RY, Wang SF, Zhang Y*, Wan C, Ma P. Toughening Modification of PLLA/PBS Blends via In Situ Compatibilization. Polymer Engineering and Science. 49, 26-33, 2009.
4) Wang, RY ; Wang, SF ; Zhang, Y*. Morphology, Mechanical Properties, and Thermal Stability of Poly(L-lactic acid)/Poly(butylene succinate-co-adipate)/Silicon Dioxide Composites. Journal of Applied Polymer Science. 113, 3630-3637, 2009